Alumilite Water Clear Casting Resin - 2 lb Kit

In stock
Not rated yet

Alumilite Water Clear produces a high impact rigid clear casting that is commonly used for lenses, encapsulations, and water reproductions. Vacuum or pressure is recommended to achieve 100% bubble free castings. The Water Clear has a new 15-minute open time and a 2-3 hour demold time.  

 

  • $43.55
Qty:  
  • Weight
    35 oz
  • SKU
    DC-10055

Alumilite Water Clear Casting Resin - 2 lb Kit

Alumilite Water Clear produces a high impact rigid clear casting that is commonly used for lenses, encapsulations, and water reproductions. Vacuum or pressure is recommended to achieve 100% bubble free castings. The Water Clear has a new 15-minute open time and a 2-3 hour demold time. 

Alumilite Clear must be mixed 1:1 by weight. Off-ratio mixing may produce hazy or frosted parts.

Recommended for industrial use only. B side may thicken and need to be warmed before use.

Alumilite is sold and mixed by weight.  2 lb kit includes 1 lb of side A and  1 lb of side B, mixing cups & stir sticks. 

 

Alumilite Water Clear Instruction Sheet

 

Customer reviews
There are no comments yet. Be the first to leave a comment
Please sign in to add review

Product questions

  • Keron mcpherson
    Jul 13, 2023, 09:06 PM

    Why some allumilite resin stay soft or bendy after d

    Administrator
    Jul 13, 2023, 10:25 PM

    After demolding? Are you using water clear or one of the "amazing" products? If the resin you are using has the word "amazing" on the product, it is an epoxy resin. Epoxies typically take much longer to cure and harden (several days, depending on thickness), and it is not unusual for epoxies to be "bendy" if taken out of the mold too early. Incorrect measurements of parts A & B, insufficient mixing, and the type and overuse of dye/additives will also affect the cure. Each type of resin is different. Make to carefully read and follow the directions for the type of resin that you are using.

Product Alumilite Water Clear
Color Clear
Mix Ratio (wt. or Vol.) 1:1 by weight
Pot Life (100g mass @ 75 degrees F) 15 minutes
Demold Time (100g mass @ 75 degrees F) 2-3 hours
Mixed Viscosity (cps.) 400
Specific Gravity 1.05
Shore Hardness (ASTM D-2240) 72 D
Shrinkage (in./in.) .005
Tensile Strength (ASTM D-638) (psi) 3,120
Elongation (in./in.) 30-40%
Temperature Resistance 140F